MICROPLASTIC DEFORMATION BEHAVIOUR OF STEEL 1Cr18Ni9Ti

ZHU Ping ZHANG Lining Southeast University , Nanjing , China ZHANG Lining Professor , Department of Materials Science and Engineering.Southeast University , Nanjing 210018 , China

金属学报(英文版)

The regularity and mechanism of the microplastic deformation of steel 1Cr18Ni9Ti both solu- tion-treated and prestrained were investigated.In the different stages of microplastic deformation,stage 1 corresponds to the dislocation moving and exhausting in the regions near grain boundaries.Stage 2,being the early stage of macroplastic deformation,corresponds to the extensive operation and generation of dislocations in the interior of grains and also dislo- cation emission from the grain boundaries.The regularities of the effect of prestrain on macro-and micro-yield strength are different.

关键词: microplasticity , null , null

ATOMIC FORCE MICROSCOPY OBSERVATION OF MAGNETRON SPUTTERED ALUMINUM-SILICON ALLOY FILMS

金属学报(英文版)

粒裕希停桑谩。疲希遥茫拧。停桑茫遥希樱茫希校佟。希拢樱牛遥郑粒裕桑希巍。希啤。停粒牵危牛裕遥希巍。樱校眨裕裕牛遥牛摹。粒蹋眨停桑危眨停樱桑蹋桑茫希巍。粒蹋蹋希佟。疲桑蹋停?##2##3##4##5ATOMICFORCEMICROSCOPYOBSERVATIONOFMAGNETRONSPUTTEREDALUMINUM-SILICONALLOYFILMSJ.W.Wu,J.H.FangandZ.H.Lu(NationalLaboratoryofMoleculeandBiomoleculeElectronics,SoutheastUniversity,Nanjing210096,ChinaManuscriptreceived27October1995)Abstrcat:Twodifferentsurfacemorphologycharacteristicsofmagnetronsputteredaluminumsilicon(Al-Si)alloyfilmsdepositedat0and200℃wereobservedbyatomicforcemicroscopy(AFM).Oneisirregularlyshapedgrainsputtogtheronaplane.TheotherisirregularlyshapedgrainsPiledupinspace.Nanometer-sizedparticleswithheightsfrom1.6to2.9nmwerefirstobserved.Onthebasisoftheseobservationsthegrowthmechanismofmagnetronsputteredfilmsisdiscussed.Keywords:magnetronsputtering,Al-Sialloy,surfacemorphology,atomicforcemicroscopy,filmgrowthmechanism1.IntroductionTheuseofaluminumalloys[1,2],inparticularAl-Si,isacommonfeatureinmanysinglelevelandmultilevelinterconnectionschemesadoptedinthemanufactureofmicroelectronicdevicesbecauseofseveraldesirableproperties.TheAl-Sigrainmorphology(size.geometryanddistributionofgrainsisassociatedwithstepcoverage[3],electromigration[4]andinterconnectsresistivity[5]etc..Thus,characterizationofAl-Sialloysurfacemorphologyisveryimportant,especiallywhenintegratedintensityincreasesandlinewidthsof0.3to0.5μmbecomecommon.Inthepasttwentyyears,theAl-Sialloysurfacemorphologywhichaffectsthereliabilityofmicroelectronicdeviceshasbeenwidelyinvestigatedbyscanningelectronmicroscopy(SEM),transmissionelectronmicroscopy(TEM)etc.[5-7].However,SEMandTEMhavetheirlimitationorinconvenience,forexample,theverticalresolutionofSEMisnothighandTEMneedscomplexsamplepreparation.Recently,anewgrainboundaryetchingmethodwasproposed ̄[8]whichalsoneedstroublesomechemicaletching.Atomicforcemicroscopy(AFM),sinceitsemerging,hasbecomemoreandmoreusefulinphysics,chemistry,materialsscienceandsurfacescience,becauseofitshighresolution,easeofsamplepreparationandrealsurfacetopography.Recently,discussion[9,10]waspresentedonhowAFMwillplayaroleinsemiconductorindustry.Asaresponsetothisdiscussion,weusedAFMtoinvestigateAl-SialloysurfacemorphologyandhaveobtainedsomeresultswhichcannotberevealedbySEMorTEM.ThisindicatesthatAFMisagoodcharacterizationtoolinsemiconductorindustry.2.SamplePreparationInourexperiments,aluminumwith30ppmsiliconwassputteredonsiliconsubstrateinbatchdepositionmodeAllthreefilmswiththicknessof1.6μmweredepositedusinganargonsputteringpressureof4.2×10 ̄-3Pa.TheotherdepositionparametersaredescribedinTable1.Thesubstratewascleanedusingstandardpremetallizationcleaningtechniquespriortofilmdeposition.3.ExperimentalResultsandDiscussionTheAFMmeasurementswereperformedonacommercialsystem(NanoscopeIII,DigitalInstruments,SantaBarbara).Thetipismadeofmicrofabricatedsiliconnitride(Si_3N_4)Itisattachedtoa200μmcantileverwithaforceconstantofabout0.12N/m.Beforethesurfaceofsamplewasexamined.agoodtipwithananometer-sizedprotrusionatitsendwasselectedbeforehand,whichcanbeobtainedbyimagingtheatomicstructureofmicasubstrateandagoldgrid.AtypicaloperatingforcebetweenthetipandAl-Sisamplesurfaceisoftheorderof10 ̄-8Nandallimagesweretakenatroomtemperatureinair.AtypicaltopographicviewoftheAl-SifilmsisshowninFig.1(allimagescansizeis5by5μma,bandcarerespectivelyforsample1,2,and3).FromFig.la,itcanbeseenthatirregularlyshapedgrainstiltinginvaryingdegreespileupinspace,andgroovesamongtheirregularlyshapedgrainsaredifficulttodecideatacertainarea(wedefineitascharacteristicA).Toourknowledge,onreportsonthesurfacemorphologyhavebeenpresentedbefore.InFig1b,however,irregularlyshapedgrainsassembleonaPlaneandgroovesamongtheirregularlyshapedgrainsareeasytodecide(wedefineitascharacteristicB),whichisinagreementwithmanypreviousreports[5-7].InFig.1c,bothcharacteristicA(arrowA)andcharacteristicB(arrowB)wereobserved.IndoingAFMexperiments,weselectedfivedifferentscanareastobeimagedforeachsampleandfoundthatallimagesofeachsamplearerespectivelysimilartoFig.1a,bandc.Also,wenotedthatthesurfaceofinFig.1a.WethinkthatdepositionparameterswillinfluenceAl-Sisurfacemorphology,andthetiltedgrainsmaybesusceptibletomicrocracking.Byreducingthescansizeareato2by2μm(Fig.2aandb).Weobtainedmanyidenticalresultsasdescribedabove,suchasirregularlyshapedgrainsetc.Forthefirsttime,wefoundnanometersizedparticlesonirregularlyshapedgrainsurfacewhichcannotberevealedbySEMbecausethediameterofthesenanoparticlesisabout10nmandtheheightofthesenanoparticlesisintherangeof1.6to2.9nm.Inimaging,wenotedthatrotatingthescandirectionandchangingthescanfrequencydidnotaffectthestructureofthesegrainsasshowninFig.2aandb,rulingoutthepossibilitythatscanninginfluencedtheshapeoftheseparticlesorcausedsomesimilarimagingartifacts.Also,wenotedthatthenanoparticleswerenotobservedontheslopesofthegrooves(Fig.2aandb).Thisphenomenoncanbeexplainedasfollows:thepotentialenergyattheslopeislargerthanthatelsewhere,sotheparticlesseemmorelikelytobedepositedontheseareaswithlowerpotentialenergy.Fig.2c,scansize250by250nm,isazoomtopographicimage(whiteoutlineinb).Itshowsunevendistributionofthenanoparticles.Andtheheightdifferenceofthenanoparticlesindicatesdifferentgrowingspeed.Wethinkbasedonthemorphologyofnanoparticles,thattheheightdifferenceandunevendistributionofthesenanoparticlesshowdifferentgrowingadvantageandindicatethatatomshaveenoughenergytomovetoasuitablegrowingspot.Theenergymaybefromthefollowingsources:surfacetemperaturefluctuation,stressdifferenceorcollisionbetweenhighspeedsputteredatoms.Thesenanoparticlesgoongrowingandformmanyirregularlyshapedgrains.AndtheseirregularlyshapedgrainsfurtherconnecteachotheraccordingtocharacteristicAorB,finallyformingtheAl-Sisurfacemorphology.4.ConclusionWecandrawthefollowingconclusionsfromtheabove.First,theexperimentalresultsshowedthatAFMisapowerfultooltoinvestigatethedetailsofAl-Sisurfacemorphologywhichcangreatlyenrichourknowledgeofthefilmgrowthmechanism.Second,depositionconditionsplayanimportantroleindeterminingtheAl-Sisurfacemorphology.Third,thetwoAl-Sisurfacemorphologycharacteristicsarethatirregularlyshapedgrainsassembleonaplaneandirregularlyshapedgrainstiltinginvaryingdegreespileupinspace.Fourth,forthefirsttime,nanoparticleswereobservedonirregularlyshapedgrainsurfacewhichsuggestedthatthefilmgrowthmechanismwasbyinhomogeneousnucleation.Acknowledgements-BeneficialdiscussionswereheldwithDr.ZhenandMr.Zhu.ThisworkwaspartiallysupportedbytheNationalNaturalScienceFoundationofChina.RFFERENCES||1D.pramanikandA.N.Saxena,SolidStateTechnol.26(1983)127.2D.pramanikandA.N.Saxena,SolidStateTechnol.26(1983)131.3D.pramanikandA.N.Saxena,SolidStateTechnol.33(1990)73.4S.S.IyerandC.Y.Worg,J.Appl.phys.57(1985)4594.5J.F.Smith,SolidStateTechnol.27(1984)135.6D.GerthandD.Katzer,ThinSolidFilm208(1992)67.7R.J.WilsonandB.L.Weiss,ThinSolidFilm207(1991)291.8E.G.Solley,J.H.Linn,R.W.BelcherandM.G.Shlepr,SolidStateTechnol33(1990)409I.SmithandRHowland,SolidStateTechnol.33(1990)53.10L.Peters,SemiconductorInternational16(1993)62.##61D.pramanikandA.N.Saxena,SolidStateTechnol.26(1983)127.2D.pramanikandA.N.Saxena,SolidStateTechnol.26(1983)131.3D.pramanikandA.N.Saxena,SolidStateTechnol.33(1990)73.4S.S.IyerandC.Y.Worg,J.Appl.phys.57(1985)4594.5J.F.Smith,SolidStateTechnol.27(1984)135.6D.GerthandD.Katzer,ThinSolidFilm208(1992)67.7R.J.WilsonandB.L.Weiss,ThinSolidFilm207(1991)291.8E.G.Solley,J.H.Linn,R.W.BelcherandM.G.Shlepr,SolidStateTechnol33(1990)409I.SmithandRHowland,SolidStateTechnol.33(1990)53.10L.Peters,SemiconductorInternational16(1993)62.##A##BATOMIC FORCE MICROSCOPY OBSERVATION OF MAGNETRON SPUTTERED ALUMINUM-SILICON ALLOY FILMS$$$$J.W.Wu,J.H. Fang and Z.H.Lu (National Laboratory of Molecule and Biomolecule Electronics,Southeast University,Nanjing 210096, China Manuscript received 27 October 1995)Abstrcat:Two different surface morphology characteristics of magnetron sputtered aluminumsilicon(Al-Si)alloy films deposited at 0 and 200℃ were observed by atomic force microscopy(AFM).One is irregularly shaped grains put togther on a plane.The other is irregularly shaped grains Piled up in space. Nanometer-sized particles with heights from 1.6 to 2.9 nm were first observed. On the basis of these observations the growth mechanism of magnetron sputtered films is discussed.

关键词: :magnetron sputtering , null , null , null , null

  • 首页
  • 上一页
  • 1
  • 2
  • 3
  • 4
  • 5
  • 下一页
  • 末页
  • 共7页
  • 跳转 Go

出版年份

刊物分类

相关作者

相关热词